AKROMID®
A3 K6 FR blue (6752)PA66 GF30 FR(40)
AKROMID® A3 K6 FR blue (6752) is a 30% glass fibre reinforced and flame retardant PA 6.6. colored in blue similar RAL 5015. The flame retardant system is free of halogens and red phosphorus. Due to its high stiffness and strength, the material is suitable for circuit breaker and housings in E&E industry.
Features
Properties
10.500MPa
120MPa
Na
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Oxygen index
ISO 4589-2
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Documents
Discover all the technical specifications at a single glance here.
Processing information
The values mentioned are recommendations. We only recommend desiccant / dry air dryers or vacuum dryers. Too long a drying time and the resulting residual moisture content below the lower limit can lead to filling problems and surface defects. The specified drying time refers to closed and undamaged bagged material. When processing from previously opened bags or from octabins with polyolefin inliners, a longer drying time may be necessary. It is recommended to check the residual moisture content after the drying process.
Drying time
2 - 4 h
Drying temperature (τ ≤ -30°C)
80 °C
Processing moisture
0,02 - 0,08 %
Feed section
60 - 80 °C
Temperature Zone 1 - Zone 4
260 - 290 °C
Nozzle temperature
260 - 300 °C
Melt temperature
270 - 290 °C
Mold temperature
60 - 100 °C
Holding pressure, spec.
300 - 800 bar
Back pressure, spec.
30 - 100 bar
Injection speed
medium
Screw speed
5 - 10 m/min
Applications
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.