AKROLOY®

PARA GF 35 FR black (7496)PARA GF 35 FR (40)

AKROLOY® PARA GF 35 FR black (7496) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.

Features

electrically neutral
flame retardant
surface modified
reduced moisture
easy flow
E&E

Properties

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
55 kJ/m²
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
13 kJ/m²
14 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
235 °C

Flammability


UL

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
825 °C

General properties


Density

ISO 1183

23°C
1,48 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 1,0 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,4 - 0,6 %

Electrical Properties


Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.