AKROLEN®

Internal

PP LGF 40 2 black (6911)PP LGF40

AKROLEN® PP LGF 40 2 black (6911) is a polypropylene homopolymer with 40% long glass fibre reinforcement which leads to a very high stiffness and strength. The materials very good surface quality as well as the outstanding UV-stability make it the product of your choice for technical parts which are exposed to UV radiation.

Features

UV-stabilised

Properties

Modulus

10.000MPa

Strength

140MPa

Impact

75kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
200 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
75 kJ/m²
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
30 kJ/m²
32 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
165 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
165 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,22 g/cm³

Electrical Properties

Volume resistivity

IEC 62631-3-1

d.a.m.
1012 Ω x cm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.