Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
554 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GF 35 1 natural (2465)

PA6 GF35

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

Preliminary

K GF 50 ECO black (8270)

PBT-PET- GF 50

PRECITE® K GF 50 ECO black (8270) - PBT/PET blend, recycled PET content, 50% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

17.000MPa

Strength

180MPa

Impact

66kJ/m²

PRECITE® K GF 50 ECO black (8270) - PBT/PET blend, recycled PET content, 50% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR black (8342)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR black (8342) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID® B28 GF 30 9 FR black (8342) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

AKROMID®

Preliminary

T9 GF 15 FR LA black (8197)

PPA GF15 FR(40)

AKROMID® T9 GF 15 FR LA black (8197) - PPA, 15% GF, flame retardant, laser markable, medium stiffness and strength, high temperature and chemical resistance.

Modulus

6.000MPa

Strength

107MPa

Impact

48kJ/m²

AKROMID® T9 GF 15 FR LA black (8197) - PPA, 15% GF, flame retardant, laser markable, medium stiffness and strength, high temperature and chemical resistance.

AKROMID®

B3 GF 50 4 RM-M black (3221)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

Modulus

16.500MPa

Strength

210MPa

Impact

75kJ/m²

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

134580

AKROMID®

B3 GK 50 black (2311)PA6 GB50

AKROMID® B3 GK 50 black (2311) is a PA 6 filled with 50% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

low warpage

Properties

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

Sustainability

Recycled content

50 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5700 MPa
2000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
75 MPa
45 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
> 10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
5200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
135 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
42 kJ/m²
32 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
3 kJ/m²
7 kJ/m²
1 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
75 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
188 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,54 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 %

Water absorption

ISO 62

23°C, saturated
4,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,6 - 0,8 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

Test liquid A
500 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.