A3 2 S1 white (5973)
PA66-I
AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture
1.700MPa
45MPa
180kJ/mĀ²
AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture
AKROMIDĀ®
S3 GF 15 5 black (6062)
PA610 GF15
AKROMIDĀ® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.
5.500MPa
120MPa
65kJ/mĀ²
AKROMIDĀ® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.
AKROMIDĀ®
A3 GF 30 6 natural (6398)
PA66 GF30
AKROMIDĀ® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength
10.000MPa
200MPa
85kJ/mĀ²
AKROMIDĀ® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength
AKROMIDĀ®
T5 ICF 20 black (6773)
PPA CF20
AKROMIDĀ® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
18.000MPa
222MPa
37kJ/mĀ²
AKROMIDĀ® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
AKROMIDĀ®
B28 GM 5/25 FR black (7492)
PA6 (GF5+GB25) FR(40)
AKROMIDĀ® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength
5.000MPa
55MPa
30kJ/mĀ²
AKROMIDĀ® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength
AKROMIDĀ®
T9 ICF 20 6 black (7907)
PPA CF 20
AKROMIDĀ® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
14.000MPa
190MPa
35kJ/mĀ²
AKROMIDĀ® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
T5 GF 40 6 natural (8003)
PPA GF40
AKROMIDĀ® T5 GF 40 6 natural (8003) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
16.000MPa
245MPa
80kJ/mĀ²
AKROMIDĀ® T5 GF 40 6 natural (8003) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROMIDĀ®
AKROMIDĀ® B3 GF 50 black (20008) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry, e.g. strut bearings.
Features
Properties
17.000MPa
210MPa
100kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 2039-1
ISO 75
ISO 75
ISO 75
ISO 11357-3
ISO 11359-1/2
IEC 60216
UL 94
IEC 60695-2-12
FMVSS 302
ISO 1183
ISO 1110
ISO 62
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.