AKROMIDĀ®

Preliminary

NEXT 5.10 3 GF 30 black (8467)

PA5.10 GF30

AKROMIDĀ® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/mĀ²

AKROMIDĀ® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

PRECITEĀ®

Preliminary

E GF 15 ECO black (8327)

E GF 15 ECO

PRECITEĀ® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

6.300MPa

Strength

110MPa

Impact

35kJ/mĀ²

PRECITEĀ® E GF 15 ECO black (8327) - PET, 15% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

P3 GF 30 9 FR black (8424)

PBT GF30 FR(40)

PRECITEĀ® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

AKROTEKĀ®

Preliminary

PK-VM GF 50 natural (8683)

PK GF50

AKROTEKĀ® PK-VM GF 50 natural (8683) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROTEKĀ® PK-VM GF 50 natural (8683) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMIDĀ® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/mĀ²

AKROMIDĀ® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

PRECITEĀ®

Preliminary

P3 GF 15 4 natural (8429)

PBT-I GF15

PRECITEĀ®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

Modulus

5.000MPa

Strength

85MPa

Impact

55kJ/mĀ²

PRECITEĀ®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

PRECITEĀ®

Preliminary

P3 GF 20 8 natural (8456)

PBT GF20

PRECITEĀ® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

7.200MPa

Strength

125MPa

Impact

65kJ/mĀ²

PRECITEĀ® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

129303180

AKROMIDĀ®

A3 GF 35 3 black (1802)PA66 GF35

AKROMIDĀ® A3 GF 35 3 black (1802) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is nucleated. It is perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

nucleated

Properties

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
4,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,7 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
> 55 kJ/mĀ²
53 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
9 kJ/mĀ²
13 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
265 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,41 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,65 - 0,85 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more