AKROMIDĀ®

UL

B3 GF 35 1 HU red (8416)

PA6 GF35

AKROMIDĀ® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

12.000MPa

Strength

190MPa

Impact

NA

AKROMIDĀ® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 black (8468)

PA6.9 GF30

AKROMIDĀ® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.

AKROTEKĀ®

Preliminary

PK-VM GF 40 natural (8682)

PK GF40

AKROTEKĀ® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

165MPa

Impact

78kJ/mĀ²

AKROTEKĀ® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

AKROTEKĀ®

Preliminary

PK-VM GF 15 natural (8680)

PK GF15

AKROTEKĀ® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

B3 GF 30 1 grey (7574)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

Modulus

9.900MPa

Strength

168MPa

Impact

NA

AKROMIDĀ® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

AKROTEKĀ®

Preliminary

PPS GF 40 black (8609)

PPS GF40

AKROTEKĀ® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

PK-VM GF 10 natural (8679)

PK GF10

AKROTEKĀ® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.600MPa

Strength

75MPa

Impact

61kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

175767780

AKROMIDĀ®

A28 LGF 50 9 black (7705)PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) is an easy flowing PA6.6 with 50% long glass fibre reinforcement which leads to an extraordinary high stiffness and strength even at high temperature. The material distinguishes itself due to its isotropic mechanical properties as well as increased creep resistance and higher heat deflection temperature. The excellent fatigue performance, high energy absorption in the event of a crash and low shrinkage make it the product of your choice for technical parts e.g. oil pan.

Features

easy flow
process improved

Properties

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18000 MPa
14200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
2,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
95 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
45 kJ/mĀ²
45 kJ/mĀ²

Izod impact strength

ISO 180/1A

23Ā°C | d.a.m.
90 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
60 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,25 10ā»ā“/K
0,75 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,57 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more