AKROMID®

UL

C3 GF 25 1 FR grey (8605)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

125MPa

Impact

50kJ/m²

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

AKROMID®

UL
Preliminary

NEXT S3 GF 15 1 HU natural (8822)

PA6.10 GF15

AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

5.000MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROTEK®

Preliminary

PK-VM GF 30 8 black (8783)

PK GF30

AKROTEK® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

AKROMID®

UL

NEXT S3 GF 50 1 HU black (8827)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

NEXT S3 GF 15 1 HU black (8823)

PA6.10 GF 15

AKROMID® NEXT S3 GF 15 1 black (8823) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® NEXT S3 GF 15 1 black (8823) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

177787980

PRECITE®

Preliminary

P3 GF 30 9 FR black (8424)PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR black (8424) is a 30% glass fibre reinforced, flame retardant polybutylene terephthalate (PBT) with high stiffness and strength. The material offers outstanding long-term heat-aging stability as well as mechanical advantages to conventional products. It achieves V0 classification at thicknesses of 1.6 mm and above by using a flame retardant system which is free of red phosphorous and halogens. Due to its low moisture absorption, this material has very good dimensional stability and it is particularly suitable for precision parts in E-Mobility or E&E industry.

Features

heat stabilised 130
flame retardant
low warpage
E&E
E-Mobility

Properties

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
122 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
197 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
50 kJ/m²
58 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
9 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
222 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
224 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
750 °C
750 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 30 %

General properties

Density

ISO 1183

23°C
1,53 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
25,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more