AKROMID®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)

PA6 GF30 FR(40)

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

AKROMID®

UL
Preliminary

NEXT S3 GF 15 1 HU natural (8822)

PA6.10 GF15

AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

5.000MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

NEXT S3 GF 15 1 HU black (8823)

PA6.10 GF 15

AKROMID® NEXT S3 GF 15 1 black (8823) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® NEXT S3 GF 15 1 black (8823) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

NEXT S3 GF 50 1 HU black (8827)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 black (8827) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

AKROMID®

UL

NEXT S3 GF 50 1 HU natural (8826)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 50 1 natural (8826) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

177787980

AKROMID®

A3 GM 25/15 1 black (7003)PA66 (GF25+GB15)

AKROMID® A3 GM 25/15 1 black (7003) is a 25% glass fiber and 15% glass beads reinforced, heat stabilised PA 6.6. The material impresses with a good surface appearance and low warpage and is therefore perfectly suitable for technical demanding components in the mechanical engineering and automotive industry.

Features

heat stabilised 130
low warpage

Properties

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10000 MPa
7000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
10200 MPa
7500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
275 MPa
205 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,4 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
70 kJ/m²
80 kJ/m²
57 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
10 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,46 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more