AKROTEK^®

PPS GF 40 black (8609)

PPS GF40

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PK-VM GF 15 natural (8680)

PK GF15

AKROTEK® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

AKROMID^®

A3 GF 50 4 natural (71090)

PA66 GF50

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

18.000MPa

Strength

260MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

AKROTEK^®

Preliminary

PPS GF 30 black (8610)

PPS GF30

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

175MPa

Impact

45kJ/m²

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK^®

Preliminary

PK-VM GF 40 black (8687)

PK GF40

AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

160MPa

Impact

80kJ/m²

AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

AKROTEK^®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROMID^®

A3 S3 natural (1176)

PA66-I

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

1 76 77 7880

AKROMID^®

C3 GF 25 1 FR black (7246)PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR black (7246) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in black. Listed to UL 94 in black V0 @ 0,4 mm and all-colours V0 @ 0,8mm, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for applications with high strength requirements in the automotive and E&E markets.

Features

heat stabilised 130

flame retardant

surface modified

easy flow

E&E

Regulatory

Properties

Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

9100 MPa

6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

137 MPa

95 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

3,0 %

5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

8800 MPa

6000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

225 MPa

160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

3,5 %

5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

66 kJ/m²

75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

11 kJ/m²

15 kJ/m²

Thermal Properties

RTI electrical

UL 746B

0,4mm Wall thickness

0,8mm Wall thickness

1,6mm Wall thickness

3,2mm Wall thickness

140 °C

150 °C

RTI impact

UL 746B

0,4mm Wall thickness

0,8mm Wall thickness

1,6mm Wall thickness

3,2mm Wall thickness

120 °C

125 °C

RTI strength

UL 746B

0,4mm Wall thickness

0,8mm Wall thickness

1,6mm Wall thickness

3,2mm Wall thickness

135 °C

140 °C

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

251 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

168 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Ball pressure test

IEC 60695-10-2

> 210 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

155 °C

130 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,37 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,8 - 2,0 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A

600 V

Comparative tracking index

ASTM D3638

0 PLC

Dielectric strength

IEC 60243

3 mm

12 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

High voltage arc tracking rate (HVTR)

UL 746A

1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

6 PLC

Rheological Properties

Flowability

AKRO

2 mm Thickness

480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

C3 GF 25 1 FR black (7246).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66+PA6 GF25 FR(40)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

RTI electrical

RTI impact

RTI strength

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Ball pressure test

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate 5V

GWFI

GWIT

HWI

HAI

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Comparative tracking index

Comparative tracking index

Dielectric strength

Inclined-Plane Tracking, IPT

High voltage arc tracking rate (HVTR)

High Volt, Low Current Arc Resistance

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

C3 GF 25 1 FR black (7246)PA66+PA6 GF25 FR(40)