AKROTEKĀ®

Preliminary

PK-VM GF 40 black (8687)

PK GF40

AKROTEKĀ® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

160MPa

Impact

80kJ/mĀ²

AKROTEKĀ® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant

AKROTEKĀ®

Preliminary

PPS GF 30 black (8610)

PPS GF30

AKROTEKĀ® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

175MPa

Impact

45kJ/mĀ²

AKROTEKĀ® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

PK-VM GF 40 natural (8682)

PK GF40

AKROTEKĀ® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

165MPa

Impact

78kJ/mĀ²

AKROTEKĀ® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

AKROTEKĀ®

Preliminary

AM ICF 20 black (8722)

ABSCF20

AKROTEKĀ® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

100MPa

Impact

20kJ/mĀ²

AKROTEKĀ® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROMIDĀ®

A3 GF 50 4 natural (71090)

PA66 GF50

AKROMIDĀ® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

18.000MPa

Strength

260MPa

Impact

110kJ/mĀ²

AKROMIDĀ® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 black (8468)

PA6.9 GF30

AKROMIDĀ® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.

AKROMIDĀ®

Preliminary

C3 GF 30 8 black (5657)

PA66 + PA6 GF30

AKROMIDĀ® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

9.400MPa

Strength

190MPa

Impact

82kJ/mĀ²

AKROMIDĀ® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

175767780

AKROMIDĀ®

C28 GF 25 FRT grey (8331)PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (8331) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to NCS S 3000 N. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120Ā°C is necessary.

Features

flame retardant
surface modified
easy flow
public transportation

Regulatory

en45545-2

Properties

Modulus

10.800MPa

Strength

140MPa

Impact

47kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
47 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
238 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,2 10ā»ā“/K
0,66 10ā»ā“/K

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
5VA Class
5VA Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 Ā°C
960 Ā°C
960 Ā°C
960 Ā°C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 Ā°C
800 Ā°C
800 Ā°C
850 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R1/6/7 HL2

General properties

Density

ISO 1183

23Ā°C
1,44 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
< 0,2 %
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more