AKROTEK®
PK-VM GF 40 black (8687)
PK GF40
AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
11.000MPa
160MPa
80kJ/m²
AKROTEK® PK-VM GF 40 black (8687) - Polyketon, 40% glass fibre reinforced, chemical restistant
AKROTEK®
PPS GF 30 black (8610)
PPS GF30
AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
12.000MPa
175MPa
45kJ/m²
AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
AKROTEK®
PK-VM GF 40 natural (8682)
PK GF40
AKROTEK® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant
11.000MPa
165MPa
78kJ/m²
AKROTEK® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant
AKROTEK®
AM ICF 20 black (8722)
ABSCF20
AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
13.400MPa
100MPa
20kJ/m²
AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
AKROMID®
A3 GF 50 4 natural (71090)
PA66 GF50
AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free
18.000MPa
260MPa
110kJ/m²
AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free
AKROMID®
NEXT G3 GF 30 1 black (8468)
PA6.9 GF30
AKROMID® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.
8.600MPa
160MPa
80kJ/m²
AKROMID® NEXT G3 GF 30 1 black (8468) - PA 6.9, 30% glass fibre, low moisture absorption, increased chemical resistance, good strength, good stiffness, industrial.
AKROMID®
C3 GF 30 8 black (5657)
PA66 + PA6 GF30
AKROMID® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances
9.400MPa
190MPa
82kJ/m²
AKROMID® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances
AKROMID®
NEXT U3 ICF 20 1 black (8232)PA11 CF20
AKROMID® NEXT U3 ICF 20 1 black (8232) is a Polyamide 11 reinforced with 20% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure. Furthermore, the material is suitable for Fused Filament Fabrication (FFF) for further processing in additive manufacturing.
Features
Properties
9.300MPa
110MPa
60kJ/m²
Sustainability
Biobased carbon content
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.