AKROTEK®

Preliminary

PK-VM GF 40 8 natural (6988)

PK GF40

AKROTEK® PK-VM GF 40 8 natural (6988) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

11.000MPa

Strength

150MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 40 8 natural (6988) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROLOY®

PA GF 60 black (7789)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROLOY®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/m²

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROTEK®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/m²

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMID®

UL

A3 GF 35 1 HU natural (8418)

PA66 GF35

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.900MPa

Strength

216MPa

Impact

NA

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROMID®

B3 GF 20 black (2491)

PA6 GF20

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

173747580

AKROLOY®

PARA GF 35 FR black (7496)PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR black (7496) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.

Features

electrically neutral
flame retardant
surface modified
reduced moisture
easy flow
E&E

Properties

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
55 kJ/m²
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
13 kJ/m²
14 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
235 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,23 10⁻⁴/K
0,36 10⁻⁴/K

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
825 °C

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 1,0 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

1 mm
30 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more