AKROLOY®
PA GF 60 LA black (8168)
PA66 + PA6I/6T GF60
AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.400MPa
275MPa
95kJ/m²
AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
NEXT 5.6 3 GF 30 S3 black (8444)
PA56 GF30
AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.
8.600MPa
180MPa
96kJ/m²
AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.
AKROMID®
B3 GF 40 1 black (2487)
PA6 GF40
AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.
AKROMID®
B3 ICF 40 black (5020)
PA6 CF40
AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
30.000MPa
220MPa
60kJ/m²
AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROTEK®
PK-VM ICF 15 black (6074)
PK CF15
AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.
9.000MPa
90MPa
30kJ/m²
AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.
AKROTEK®
PK-VM 8 black (6466)
PK
AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011
1.600MPa
60MPa
180kJ/m²
AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011
AKROMID®
B+ GF 30 6 LT black (7665)
PA6 GF30
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
10.000MPa
185MPa
95kJ/m²
High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
AKROMID®
B28 GF 30 S3 natural (8348)PA6-I GF30
AKROMID® B28 GF 30 S3 natural (8348) is a 30% glass fibre reinforced, easy flowing polyamide 6. Furthermore, the material is impact modified and therefore characterised by a higher dry impact strength compared to standard PA 6 GF 30. Its high strength and stiffness make it the material of your choice for technical applications in industrial engineering and in the furniture industry. The material has a light inherent color.
Features
Properties
8.900MPa
160MPa
100kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.