Description

AKROLOY®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/m²

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/m²

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMID®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

AKROMID®

B3 ICF 40 black (5020)

PA6 CF40

AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

30.000MPa

Strength

220MPa

Impact

60kJ/m²

AKROMID® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROTEK®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/m²

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

AKROTEK®

PK-VM 8 black (6466)

PK

AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

169707180

AKROMID®

B3 1 natural (2499)PA6

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

Features

heat stabilised 130

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Water absorption

ISO 62

23°C, saturated
9,0 - 10,0 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.