AKROLOYĀ®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/mĀ²

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMIDĀ® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/mĀ²

AKROMIDĀ® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMIDĀ®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMIDĀ® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

AKROMIDĀ®

B3 ICF 40 black (5020)

PA6 CF40

AKROMIDĀ® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

30.000MPa

Strength

220MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 ICF 40 black (5020) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROTEKĀ®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEKĀ® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/mĀ²

AKROTEKĀ® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

AKROTEKĀ®

PK-VM 8 black (6466)

PK

AKROTEKĀ® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

AKROMIDĀ®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/mĀ²

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

169707180

AKROMIDĀ®

A3 GM 20/10 S1 natural (1217)PA66-I (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 S1 natural (1217) is a 20% glass fiber and 10% glass beads reinforced, impact modified PA 6.6. It is characterised by a medium cold impact strength as well as good adhesion properties. Furthermore, the material impresses with a good surface appearance and low warpage and is therefore perfectly suitable for technical demanding components in the mechanical engineering and automotive industry. It has a light inherent color.

Features

impact modified
surface modified
low warpage
adhesion modified

Properties

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/mĀ²

Sustainability

Recycled content

10 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6900 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
130 MPa
85 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6900 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
205 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
80 kJ/mĀ²
80 kJ/mĀ²
76 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
15 kJ/mĀ²
16 kJ/mĀ²
8 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
127 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,27 10ā»ā“/K
1,11 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,31 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2 %

Water absorption

ISO 62

23Ā°C, saturated
5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 - 0,6 %
0,9 - 1,1 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.