AKROMID®

S3 GF 30 4 natural (3552)

PA6.10

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/m²

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

AKROLOY®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

AKROTEK®

Preliminary

PK-VM GF 15 8 black (6991)

PK GF15

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

4.500MPa

Strength

95MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

PRECITE®

Preliminary

E GF 20 natural (7301)

PET GF 20

PRECITE® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

145MPa

Impact

40kJ/m²

PRECITE® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

High-heat stabilised, laser transparent PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMID®

Preliminary

NEXT U3 ICF 20 1 black (8232)

PA11 CF20

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

AKROMID®

UL

A3 GF 35 1 HU natural (8418)

PA66 GF35

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

11.900MPa

Strength

216MPa

Impact

NA

AKROMID® A3 GF 35 1 HU natural (8418) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

166676880

AKROTEK®

PK-HM natural (7536)PK

PK-HM natural (7536) is an unreinforced, purified Polyketone with average flowability. The outstanding friction and wear properties enable the use for demanding components exposed to tribological stress. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. This grade is especially designed for extrusion process.

Features

hydrolysis / chemically stabilised

Properties

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1400 MPa
1400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
60 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 300 %
> 300 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
1600 MPa
1200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
60 MPa
60 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
15 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
190 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 0,9 %

Water absorption

ISO 62

23°C, saturated
2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,4 - 1,6 %
1,5 - 1,7 %

Rheological Properties

MVR

ISO 1133

240°C/2,16kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more