Select your fitting and find the right compound for your intend
AKROMIDĀ®
T9 GF 15 S1 black (7820)
PPA-I GF15
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
5.000MPa
120MPa
73kJ/mĀ²
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
B3 GF 25 1 natural (2463)
PA6 GF25
AKROMIDĀ® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color
8.500MPa
160MPa
85kJ/mĀ²
AKROMIDĀ® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color
AKROMIDĀ®
B3 LA black (4056)
PA6
AKROMIDĀ® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry
3.400MPa
85MPa
180kJ/mĀ²
AKROMIDĀ® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry
AKROMIDĀ®
A28 GF 40 1 natural (4919)
PA66 GF40
AKROMIDĀ® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
13.000MPa
245MPa
95kJ/mĀ²
AKROMIDĀ® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
B3 3 natural (5772)
PA6
AKROMIDĀ® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
3.200MPa
80MPa
NA
AKROMIDĀ® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland
AKROMIDĀ®
B3 GF 20 1 black (2483)
PA6 GF20
AKROMIDĀ® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength
6.800MPa
150MPa
73kJ/mĀ²
AKROMIDĀ® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength
AKROLENĀ®
PP LGF 40 2 black (8488)
PP LGF40
AKROLENĀ® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
10.100MPa
140MPa
81kJ/mĀ²
AKROLENĀ® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.
AKROMIDĀ®
NEXT B3 GF 30 1 L CR black (8313)PA6 + PP GF30
AKROMIDĀ® NEXT B3 GF 30 1 L CR black (8313) is a PA6/PP-blend with reduced density compared to standard PA6 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where weight reduction are required. The chemical resistance is particularly superior to calcium chloride (CaClā). The material is certified according to REDcertĀ². 34% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (ā allocation factor).
Features
Regulatory
Properties
8.800MPa
140MPa
70kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.