T9 GF 15 S1 black (7820)

PPA-I GF15

AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Modulus

5.000MPa

Strength

120MPa

Impact

73kJ/mĀ²

AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

AKROMIDĀ®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMIDĀ® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

AKROMIDĀ®

B3 LA black (4056)

PA6

AKROMIDĀ® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

Modulus

3.400MPa

Strength

85MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

AKROMIDĀ®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMIDĀ® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/mĀ²

AKROMIDĀ® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B3 3 natural (5772)

PA6

AKROMIDĀ® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland

Modulus

3.200MPa

Strength

80MPa

Impact

NA

AKROMIDĀ® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland

AKROMIDĀ®

B3 GF 20 1 black (2483)

PA6 GF20

AKROMIDĀ® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/mĀ²

AKROMIDĀ® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

AKROLENĀ®

Preliminary

PP LGF 40 2 black (8488)

PP LGF40

AKROLENĀ® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/mĀ²

AKROLENĀ® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

161626380

AKROMIDĀ®

A3 ICF 40 black (5116)PA66 CF40

AKROMIDĀ® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Properties

Modulus

33.000MPa

Strength

270MPa

Impact

60kJ/mĀ²

Sustainability

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
33000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,5 %
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
30000 MPa
22000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
370 MPa
300 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
1,8 %
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
60 kJ/mĀ²
70 kJ/mĀ²
55 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
9 kJ/mĀ²
12 kJ/mĀ²
7 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
265 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
235 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,04 10ā»ā“/K
0,78 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
155 Ā°C
130 Ā°C

Thermal conductivity

DIN 52612

0,47 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
103 ā„¦
103 ā„¦

Rheological Properties

Flowability

AKRO

2 mm Thickness
360 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more