AKROMID®

Preliminary

T9 GF 15 S1 black (7820)

PPA-I GF15

AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Modulus

5.000MPa

Strength

120MPa

Impact

73kJ/m²

AKROMID® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

AKROMID®

B3 LA black (4056)

PA6

AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

Modulus

3.400MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

AKROMID®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/m²

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 3 natural (5772)

PA6

AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland

Modulus

3.200MPa

Strength

80MPa

Impact

NA

AKROMID® B3 3 natural (5772) - PA6, unreinforced, nucleated, lubricated, Dryblend, furniture industry, automotive, cable gland

AKROMID®

B3 GF 20 1 black (2483)

PA6 GF20

AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

AKROLEN®

Preliminary

PP LGF 40 2 black (8488)

PP LGF40

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

161626380

AKROMID®

B3 GF 50 2 S1 black (3050)PA6-I GF50

AKROMID® B3 GF 50 2 S1 black (3050) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. Furthermore, it is UV stabilised. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry.

Features

UV-stabilised
impact modified

Properties

Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15000 MPa
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
195 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
110 kJ/m²
> 110 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
27 kJ/m²
40 kJ/m²
20 kJ/m²
20 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,54 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more