Description

AKROMID®

S3 8 natural (4881)

PA610

AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

Modulus

2.300MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

AKROLEN®

Preliminary

PP LGF 40 2 black (8488)

PP LGF40

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® PP LGF 40 2 schwarz (8488) - Polypropylen copolymer, long glass fiber very high stiffness, very high strength, good surface, UV stabilised, sports & leisure, household, industrial.

AKROMID®

B3 GF 30 S1 white (3767)

PA6-I GF30

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

160MPa

Impact

105kJ/m²

AKROMID® B3 GF 30 S1 white (3767) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/m²

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 35 1 black (20017)

PA6 GF35

AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

185MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 20 1 natural (2462)

PA6 GF20

AKROMID® B3 GF 20 1 natural (2462) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color.

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 1 natural (2462) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color.

159606180

AKROMID®

Preliminary

S3 GF 30 4 black (3429)PA610 GF30

AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.

Features

hydrolysis / chemically stabilised
reduced moisture

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/m²

Sustainability

Biobased carbon content

57 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5,5 %
6,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
5,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
110 kJ/m²
90 kJ/m²
110 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
16 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
195 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
140 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.