AKROMID®

UL
Preliminary

B28 GF 35 9 FR black (8189)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR grey (8505)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR grey (8505) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, grey, e-mobility.

Modulus

11.000MPa

Strength

135MPa

Impact

80kJ/m²

AKROMID® B28 GF 30 9 FR grey (8505) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, grey, e-mobility.

PRECITE®

P3 S1 black (7522)

PBT I

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

Modulus

1.750MPa

Strength

40MPa

Impact

180kJ/m²

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

PRECITE®

Preliminary

K GF 50 ECO black (8270)

PBT-PET- GF 50

PRECITE® K GF 50 ECO black (8270) - PBT/PET blend, recycled PET content, 50% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

17.000MPa

Strength

180MPa

Impact

66kJ/m²

PRECITE® K GF 50 ECO black (8270) - PBT/PET blend, recycled PET content, 50% glass fiber, high strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROLOY®

UL

PARA GF 60 HU black (8519)

PARA GF60

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

UL
Preliminary

B28 GF 25 9 FR black (8250)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

Preliminary

NEXT G3 GF 30 1 natural (8085)

PA6.9 GF30

AKROMID® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/m²

AKROMID® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

156780

AKROMID®

Internal

B3 natural (2500)PA6

AKROMID® B3 natural (2500) is an unreinforced polyamide 6 with light inherent color

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Water absorption

ISO 62

23°C, saturated
9,0 - 10,0 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more