Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
B3 LA black (4056)
PA6
AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry
3.400MPa
85MPa
180kJ/m²
AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry
AKROMID®
T9 GF 35 4 black (7858)
PPA GF35
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/m²
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
A3 1 S3 grey (2955)
PA66+PA6-I
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
68MPa
180kJ/m²
AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMID®
A3 GF 13 S3 black (3768)
PA66-I GF13
AKROMID® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry
5.200MPa
125MPa
75kJ/m²
AKROMID® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry
AKROMID®
S3 8 natural (4881)
PA610
AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact
2.300MPa
65MPa
180kJ/m²
AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact
AKROMID®
B3 GF 15 8 L natural (5689)
PA6+PP GF15
AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011
5.200MPa
110MPa
65kJ/m²
AKROMID® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011
AKROMID®
A3 GF 25 FR natural (7649)
PA66 GF25 FR(40)
AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color
9.200MPa
135MPa
63kJ/m²
AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color
AKROLOY®
PA GF 50 8 black (6732)PA66+PA6I/6T GF50
AKROLOY® PA GF 50 8 black (6732) is a 50% glass fiber reinforced, semi-aromatic polyamide blend. It is characterised by lower moisture absorption compared to standard PA 6.6 compounds, thus convincing through very high stiffness and strength even in the conditioned state. The material is therefore perfectly suitable for technical applications with high demands for dimensional stability. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys. The compound fulfill FDA, EU10/2011 and ACS.
Features
Regulatory
Properties
17.500MPa
260MPa
105kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.