Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
B3 GF 10 natural (2829)
PA6 GF10
AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.
4.800MPa
105MPa
47kJ/m²
AKROMID® B3 GF 10 natural (2829) is a 10% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color.
AKROLOY®
PA GF 40 black (2845)
PA66 + PA6I/6T GF40
AKROLOY® PA GF 40 black (2845) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 40 black (6416) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
13.000MPa
230MPa
95kJ/m²
AKROLOY® PA GF 40 black (2845) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 40 black (6416) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
AKROMID®
A3 GF 13 S3 black (3768)
PA66-I GF13
AKROMID® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry
5.200MPa
125MPa
75kJ/m²
AKROMID® A3 GF 13 S3 black (3768) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry
AKROMID®
S3 8 natural (4881)
PA610
AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact
2.300MPa
65MPa
180kJ/m²
AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact
AKROMID®
A3 ICF 15 black (5056)
PA66 CF15
AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
12.000MPa
170MPa
45kJ/m²
AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
B3 GF 35 1 black (20017)
PA6 GF35
AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
11.000MPa
185MPa
100kJ/m²
AKROMID® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
T9 GF 35 4 black (7858)
PPA GF35
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
11.000MPa
200MPa
75kJ/m²
AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
PRECITE®
P3 ICF 30 black (6948)PBT CF 30
PRECITE® P3 ICF 30 black (6948) is a medium viscous polybutylene terephthalate (PBT) with 30% recycled carbon fiber. Despite lower density compared to PBT with glass fiber reinforcement, the product has very high strength and toughness as well as high dimensional stability. The good tribological properties and improved surface finish make it the material of choice for precision components in the automotive, mechanical engineering, E&E and household goods industries.
Features
Properties
23.500MPa
175MPa
50kJ/m²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Surface resistivity
DIN EN 62631-3-2
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.