Description

AKROLOY®

Preliminary

PA FGF 60 black (6765)

PA66 + PA6I/6T GF 60

AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction

Modulus

20.000MPa

Strength

290MPa

Impact

90kJ/m²

AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction

AKROTEK®

PK-HM natural (7536)

PK

AKROTEK® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion

AKROLOY®

PA GF 60 beige (7632)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.300MPa

Strength

265MPa

Impact

85kJ/m²

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROLEN®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)

PP LGF40

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

AKROMID®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMID® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMID®

Preliminary

NEXT U28 ICF 30 1 black (8233)

PA11 CF30

AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility

Modulus

15.300MPa

Strength

165MPa

Impact

75kJ/m²

AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID® B28 GM 15/15 1 FR black (8750) - PA6, 15% glass fibre, 15% glass beads, flame retardant, free of halogene, high stiffness and strength, very good flowability, laser markable, E&E.

152535480

AKROMID®

Internal

B3 ICF 15 black (7402)PA6 CF15

AKROMID® B3 ICF 15 black BMW (7402) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. Please refer to the product B3 ICF 15 black (7402) which is identical in composition and specification. The BMW item can only be supplied with approval from BMW for specially promoted projects.

Features

heat stabilised 130

Properties

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9000 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
55 kJ/m²
80 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Thermal conductivity

DIN 52612

0,31 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
105 Ω
105 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.