Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

C3 1 S3 black (4297)

PA66+PA6

AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

Preliminary

B3 GF 25 1 L natural (4781)

PA6 + PP GF25

AKROMID® B3 GF 25 1 L natural (4781) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

7.200MPa

Strength

130MPa

Impact

70kJ/m²

AKROMID® B3 GF 25 1 L natural (4781) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROTEK®

PK-VM black (4973)

PK

AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMID®

A3 2 S1 white (5973)

PA66-I

AKROMID® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/m²

AKROMID® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMID®

S3 GF 15 5 black (6062)

PA610 GF15

AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.

Modulus

5.500MPa

Strength

120MPa

Impact

65kJ/m²

AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.

AKROMID®

T5 GF 30 8 black (6457)

PPA GF30

AKROMID® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

11.500MPa

Strength

210MPa

Impact

65kJ/m²

AKROMID® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMID®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

151525380

AKROMID®

T5 GF 40 8 black (7963)PPA GF40

AKROMID® T5 GF 40 8 black (7963) is a 40% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR except alcoholic beverages containing more than 8 percent alcohol. This grade is suitable for parts of kitchen and household appliances.

Regulatory

eu102011fda

Properties

Modulus

15.000MPa

Strength

235MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15000 MPa
15000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
235 MPa
230 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15600 MPa
15000 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
80 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
11 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
280 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,5 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
300 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more