AKROMIDĀ®

C3 1 S3 black (4297)

PA66+PA6

AKROMIDĀ® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMIDĀ®

Preliminary

B3 GF 25 1 L natural (4781)

PA6 + PP GF25

AKROMIDĀ® B3 GF 25 1 L natural (4781) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

7.200MPa

Strength

130MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 25 1 L natural (4781) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROTEKĀ®

PK-VM black (4973)

PK

AKROTEKĀ® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMIDĀ®

A3 2 S1 white (5973)

PA66-I

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMIDĀ®

S3 GF 15 5 black (6062)

PA610 GF15

AKROMIDĀ® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.

Modulus

5.500MPa

Strength

120MPa

Impact

65kJ/mĀ²

AKROMIDĀ® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.

AKROMIDĀ®

T5 GF 30 8 black (6457)

PPA GF30

AKROMIDĀ® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

11.500MPa

Strength

210MPa

Impact

65kJ/mĀ²

AKROMIDĀ® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMIDĀ® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

151525380

AKROTEKĀ®

PK-VM CF 10 TM black (6135)PK CF10

AKROTEKĀ® PK-VM CF 10 TM black (6135) is a 10% carbon fibre reinforced polyketone with tribological modification and a high elongation at break. The outstanding friction and wear properties enable the use for demanding components exposed to tribological stress. The most important markets for AKROTEKĀ® PK are the furniture industry and mechanical engineering.

Features

hydrolysis / chemically stabilised
tribological modified

Properties

Modulus

3.500MPa

Strength

59MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3500 MPa
3400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
59 MPa
59 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 30 %
> 30 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
100 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
6 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,27 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 - 0,6 %
0,8 - 1,0 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Rheological Properties

Flowability

AKRO

1 mm Thickness
250 mm

MVR

ISO 1133

240Ā°C/2,16kg
32 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more