HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

A3 2 S1 grey (5972)

PA66-I

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.800MPa

Strength

45MPa

Impact

NA

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMID®

B3 9 natural (6409)

PA6

AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland

Modulus

3.300MPa

Strength

85MPa

Impact

NA

AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland

AKROMID®

UL

B3 1 FR orange (7698)

PA6 FR(30)

AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.600MPa

Strength

75MPa

Impact

NA

AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

T5 GF 50 natural (7834)

PPA GF50

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

18.500MPa

Strength

275MPa

Impact

95kJ/m²

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

B3 GF 10 1 black (3658)

PA6 GF10

AKROMID® B3 GF 10 1 black (3658) is a 10% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

4.800MPa

Strength

105MPa

Impact

47kJ/m²

AKROMID® B3 GF 10 1 black (3658) is a 10% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

AKROMID®

B3 GF 50 1 grey (5507)

PA6 GF50

AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.500MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

S3 GF 15 5 black (6062)

PA610 GF15

AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.

Modulus

5.500MPa

Strength

120MPa

Impact

65kJ/m²

AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.

149505180

AKROLOY®

UL

PARA GF 60 HU black (8519)PARA GF60

AKROLOY® PARA GF 60 HU black (8519) is a 60% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.

Features

reduced moisture
easy flow
metal substitution

Regulatory

ul

Properties

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
24000 MPa
24000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
310 MPa
280 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,0 %
2,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
23500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
400 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
80 kJ/m²
85 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/C

ISO 75

8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
2 PLC
2 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,76 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.