AKROMID®

T5 GF 40 8 black (7963)

PPA GF40

AKROMID® T5 GF 40 8 black (7963) - PPA, 40% glass fiber, food contact, kitchen and household appliances

Modulus

15.000MPa

Strength

235MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 8 black (7963) - PPA, 40% glass fiber, food contact, kitchen and household appliances

AKROMID®

B3 GF 30 2 RM-D black (3424)

PA6+ABS GF30

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

Modulus

9.300MPa

Strength

145MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

AKROMID®

A3 2 S1 grey (5972)

PA66-I

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.800MPa

Strength

45MPa

Impact

NA

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROTEK®

PK-VM CF 10 TM black (6135)

PK CF10

AKROTEK® PK-VM CF 10 TM black (6135) - Polyketon, 10% carbon fiber reinforced, chemical, tribological modification, high elongation at break

Modulus

3.500MPa

Strength

59MPa

Impact

100kJ/m²

AKROTEK® PK-VM CF 10 TM black (6135) - Polyketon, 10% carbon fiber reinforced, chemical, tribological modification, high elongation at break

AKROMID®

Preliminary

T5 ICF 20 black (6773)

PPA CF20

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

Modulus

18.000MPa

Strength

222MPa

Impact

37kJ/m²

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

AKROMID®

A3 GF 50 8 natural (7291)

PA66 GF50

AKROMID® A3 GF 50 8 natural (7291) - PA6.6, 50% glass fiber, food contact, kitchen and household appliances

Modulus

17.400MPa

Strength

265MPa

Impact

115kJ/m²

AKROMID® A3 GF 50 8 natural (7291) - PA6.6, 50% glass fiber, food contact, kitchen and household appliances

AKROLOY®

PA GF 60 beige (7632)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.300MPa

Strength

265MPa

Impact

85kJ/m²

AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

148495080

AKROLOY®

UL
Internal

PA GF 60 7 black (2844)PA6+PA6I/6T GF60

AKROLOY® PA GF 60 7 black (2844) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 black (6418) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed grade.

Regulatory

ul

Properties

Modulus

22.000MPa

Strength

275MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
22000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
275 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
21200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
435 MPa
370 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
90 kJ/m²
90 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
18 kJ/m²
17 kJ/m²
18 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
330 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
240 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,55 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,72 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1017 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more