HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

A3 6 LT black (5651)

PA66

AKROMIDĀ® A3 6 LT black (5651) is an unreinforced, inorganic high temperature stabilised and laser-transparent polyamide 6.6

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 6 LT black (5651) is an unreinforced, inorganic high temperature stabilised and laser-transparent polyamide 6.6

AKROMIDĀ®

D3 GF 30 2 black (7026)

PA612 GF30

AKROMIDĀ® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector

Modulus

9.500MPa

Strength

180MPa

Impact

95kJ/mĀ²

AKROMIDĀ® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector

AKROMIDĀ®

B3 GF 40 5 black (7286)

PA6 GF40

AKROMIDĀ® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

C3 1 S3 black (4297)

PA66+PA6

AKROMIDĀ® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMIDĀ®

C3 GF 35 1 natural (4748)

PA66+PA6 GF35

AKROMIDĀ® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

200MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

A3 2 S1 white (5973)

PA66-I

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMIDĀ®

A3 2 S1 grey (5972)

PA66-I

AKROMIDĀ® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.800MPa

Strength

45MPa

Impact

NA

AKROMIDĀ® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

147484980

AKROMIDĀ®

A3 ICF 40 black (5116)PA66 CF40

AKROMIDĀ® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Properties

Modulus

33.000MPa

Strength

270MPa

Impact

60kJ/mĀ²

Sustainability

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
33000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,5 %
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
30000 MPa
22000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
370 MPa
300 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
1,8 %
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
60 kJ/mĀ²
70 kJ/mĀ²
55 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
9 kJ/mĀ²
12 kJ/mĀ²
7 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
265 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
235 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,04 10ā»ā“/K
0,78 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
155 Ā°C
130 Ā°C

Thermal conductivity

DIN 52612

0,47 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
103 ā„¦
103 ā„¦

Rheological Properties

Flowability

AKRO

2 mm Thickness
360 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.