PRECITE®

K ICF 20 4 ECO black (8795)

PBT-PET- CF 20

PRECITE® K ICF 20 4 ECO black (8795) - PBT/PET blend, 20% recycled carbon fibre, hydrolysis stabilised , very high strength, improved surface finish, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

13.600MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® K ICF 20 4 ECO black (8795) - PBT/PET blend, 20% recycled carbon fibre, hydrolysis stabilised , very high strength, improved surface finish, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

AKROTEK®

Preliminary

PK-VM GF 50 black (8688)

PK GF50

AKROTEK® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

165MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

UL
Preliminary

C3 1 FR orange (8799)

PA66+PA6 FR(30)

AKROMID® C3 1 FR orange (8799) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

NA

AKROMID® C3 1 FR orange (8799) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, public transportation, new mobility.

AKROLOY®

Preliminary

PARA GF 50 8 black (8394)

PARA GF50

AKROLOY® PARA GF 50 8 black (8394) - PARA, 50% GF, highest modulus and strength, very good flowability, good surface, low creep, food contact, FDA; EU10/2011, kitchen appliances, household appliances

Modulus

20.000MPa

Strength

290MPa

Impact

74kJ/m²

AKROLOY® PARA GF 50 8 black (8394) - PARA, 50% GF, highest modulus and strength, very good flowability, good surface, low creep, food contact, FDA; EU10/2011, kitchen appliances, household appliances

AKROMID®

Preliminary

B3 GF 35 ECO black (8472)

PA6 GF35

AKROMID® B3 GF 35 ECO black (8472) - PA 6, 35% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

Modulus

10.500MPa

Strength

160MPa

Impact

82kJ/m²

AKROMID® B3 GF 35 ECO black (8472) - PA 6, 35% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

AKROLOY®

PA GF 60 white (7973)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.000MPa

Strength

270MPa

Impact

85kJ/m²

AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

A3 GF 20 1 natural (1261)

PA66 GF20

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

141424380

AKROTEK®

Preliminary

PK-VM GF 15 natural (8680)PK GF15

AKROTEK® PK-VM GF 15 natural (8680) is a 15% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 15 natur (4705) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised

Properties

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
4600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
130 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
10 kJ/m²
10 kJ/m²
7 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
119 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,35 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,5 - 0,7 %
1,1 - 1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.