PARA GF 50 8 black (8394)

PARA GF50

AKROLOYĀ® PARA GF 50 8 black (8394) - PARA, 50% GF, highest modulus and strength, very good flowability, good surface, low creep, food contact, FDA; EU10/2011, kitchen appliances, household appliances

Modulus

20.000MPa

Strength

290MPa

Impact

74kJ/mĀ²

AKROLOYĀ® PARA GF 50 8 black (8394) - PARA, 50% GF, highest modulus and strength, very good flowability, good surface, low creep, food contact, FDA; EU10/2011, kitchen appliances, household appliances

AKROMIDĀ®

UL
Preliminary

C3 1 FR orange (8799)

PA66+PA6 FR(30)

AKROMIDĀ® C3 1 FR orange (8799) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

NA

AKROMIDĀ® C3 1 FR orange (8799) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, public transportation, new mobility.

AKROMIDĀ®

Preliminary

B3 GF 35 ECO black (8472)

PA6 GF35

AKROMIDĀ® B3 GF 35 ECO black (8472) - PA 6, 35% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

Modulus

10.500MPa

Strength

160MPa

Impact

82kJ/mĀ²

AKROMIDĀ® B3 GF 35 ECO black (8472) - PA 6, 35% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

PRECITEĀ®

K ICF 20 4 ECO black (8795)

PBT-PET- CF 20

PRECITEĀ® K ICF 20 4 ECO black (8795) - PBT/PET blend, 20% recycled carbon fibre, hydrolysis stabilised , very high strength, improved surface finish, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

13.600MPa

Strength

115MPa

Impact

50kJ/mĀ²

PRECITEĀ® K ICF 20 4 ECO black (8795) - PBT/PET blend, 20% recycled carbon fibre, hydrolysis stabilised , very high strength, improved surface finish, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

AKROLOYĀ®

PA GF 60 white (7973)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.000MPa

Strength

270MPa

Impact

85kJ/mĀ²

AKROLOYĀ® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROTEKĀ®

Preliminary

PK-VM GF 50 black (8688)

PK GF50

AKROTEKĀ® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

165MPa

Impact

60kJ/mĀ²

AKROTEKĀ® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

A3 GF 20 1 natural (1261)

PA66 GF20

AKROMIDĀ® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/mĀ²

AKROMIDĀ® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

141424380

AKROTEKĀ®

PK-VM CF 10 TM black (6135)PK CF10

AKROTEKĀ® PK-VM CF 10 TM black (6135) is a 10% carbon fibre reinforced polyketone with tribological modification and a high elongation at break. The outstanding friction and wear properties enable the use for demanding components exposed to tribological stress. The most important markets for AKROTEKĀ® PK are the furniture industry and mechanical engineering.

Features

hydrolysis / chemically stabilised
tribological modified

Properties

Modulus

3.500MPa

Strength

59MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3500 MPa
3400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
59 MPa
59 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 30 %
> 30 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
100 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
6 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,27 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 - 0,6 %
0,8 - 1,0 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Rheological Properties

Flowability

AKRO

1 mm Thickness
250 mm

MVR

ISO 1133

240Ā°C/2,16kg
32 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more