PRECITE®

K ICF 20 4 ECO black (8795)

PBT-PET- CF 20

PRECITE® K ICF 20 4 ECO black (8795) - PBT/PET blend, 20% recycled carbon fibre, hydrolysis stabilised , very high strength, improved surface finish, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

13.600MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® K ICF 20 4 ECO black (8795) - PBT/PET blend, 20% recycled carbon fibre, hydrolysis stabilised , very high strength, improved surface finish, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

AKROTEK®

Preliminary

PK-VM GF 50 black (8688)

PK GF50

AKROTEK® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

165MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

UL
Preliminary

C3 1 FR orange (8799)

PA66+PA6 FR(30)

AKROMID® C3 1 FR orange (8799) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

NA

AKROMID® C3 1 FR orange (8799) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, public transportation, new mobility.

AKROLOY®

Preliminary

PARA GF 50 8 black (8394)

PARA GF50

AKROLOY® PARA GF 50 8 black (8394) - PARA, 50% GF, highest modulus and strength, very good flowability, good surface, low creep, food contact, FDA; EU10/2011, kitchen appliances, household appliances

Modulus

20.000MPa

Strength

290MPa

Impact

74kJ/m²

AKROLOY® PARA GF 50 8 black (8394) - PARA, 50% GF, highest modulus and strength, very good flowability, good surface, low creep, food contact, FDA; EU10/2011, kitchen appliances, household appliances

AKROMID®

Preliminary

B3 GF 35 ECO black (8472)

PA6 GF35

AKROMID® B3 GF 35 ECO black (8472) - PA 6, 35% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

Modulus

10.500MPa

Strength

160MPa

Impact

82kJ/m²

AKROMID® B3 GF 35 ECO black (8472) - PA 6, 35% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

AKROLOY®

PA GF 60 white (7973)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

22.000MPa

Strength

270MPa

Impact

85kJ/m²

AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

A3 GF 20 1 natural (1261)

PA66 GF20

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

141424380

AKROLOY®

PA GF 50 natural (2916)PA66+PA6I/6T GF50

AKROLOY® PA GF 50 natural (2916) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 50 natural (6414) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Properties

Modulus

17.500MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
16500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
16400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
380 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
105 kJ/m²
100 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
17 kJ/m²
17 kJ/m²
15 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,65 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Vicat softening temperature B50

ISO 306

50°C/50N
242 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,4 %

Water absorption

ISO 62

23°C, saturated
3,5 - 4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,3 - 0,5 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1017 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Permittivity

IEC 60250

1 MHz
4,42

Rheological Properties

MVR

ISO 1133

275°C/5kg
9 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more