Select your fitting and find the right compound for your intend
AKROMID®
B3 GK 30 natural (2719)
PA6 GB30
AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.400MPa
70MPa
30kJ/m²
AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
B3 GM 15/15 natural (3079)
PA6 (GF15+GB15)
AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color
7.200MPa
130MPa
64kJ/m²
AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color
AKROMID®
B3 GF 30 RM-M natural (3291)
PA6 + X GF30
AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
11.000MPa
165MPa
70kJ/m²
AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
AKROMID®
C3 GF 30 5 XTC natural (4499)
PA66 + PA6 GF 30
AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.
9.500MPa
185MPa
95kJ/m²
AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.
AKROMID®
B3 GM 10/20 1 L black (4646)
PA6+PP (GF10+GB20)
AKROMID® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride
5.100MPa
88MPa
46kJ/m²
AKROMID® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride
AKROMID®
A3 ICF 20 black (5102)
PA66 CF20
AKROMID® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
16.000MPa
190MPa
50kJ/m²
AKROMID® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
A28 GF 35 6 black (7278)
PA66 GF35
AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
11.500MPa
210MPa
85kJ/m²
AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
AKROMID®
AKROMID® C3 5 S3 black (8029) is an unreinforced, impact modified polyamide 6.6/6 blend. It is characterised by higher dry impact strength compared to standard polyamide 6.6/6 blends while maintaining good flowability. Furthermore, the material is high heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.
Features
Properties
2.500MPa
65MPa
180kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
FMVSS 302
ISO 1183
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.