AKROMID®

A3 GM 20/10 S1 black (4817)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

AKROMID®

A28 GF 30 9 black (4915)

PA66 GF30

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

Modulus

9.600MPa

Strength

200MPa

Impact

70kJ/m²

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

AKROMID®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/m²

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROMID®

B3 GF 30 9 RM-M black (3099)

PA6+X GF30

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

Modulus

10.500MPa

Strength

170MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

AKROTEK®

PK-HM natural (4773)

PK

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

AKROLOY®

PA LGF 50 natural (5504)

PA66+PA6I/6T LGF50

AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

Modulus

19.000MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

AKROMID®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

136373880

AKROMID®

Internal

S3 GF 50 1 natural (3533)PA610 GF50

AKROMID® S3 GF 50 1 natural (3533) is a 50% glass fibre reinforced, heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption, high chemical resistance and light inherent color.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

61 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
20 kJ/m²
16 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,51 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more