AKROMID®

A3 GM 20/10 S1 black (4817)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

AKROMID®

A28 GF 30 9 black (4915)

PA66 GF30

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

Modulus

9.600MPa

Strength

200MPa

Impact

70kJ/m²

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

AKROMID®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/m²

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROMID®

B3 GF 30 9 RM-M black (3099)

PA6+X GF30

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

Modulus

10.500MPa

Strength

170MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

AKROTEK®

PK-HM natural (4773)

PK

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

AKROLOY®

PA LGF 50 natural (5504)

PA66+PA6I/6T LGF50

AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

Modulus

19.000MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

AKROMID®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

136373880

AKROLOY®

UL
Internal

PA GF 60 7 black (2844)PA6+PA6I/6T GF60

AKROLOY® PA GF 60 7 black (2844) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 black (6418) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed grade.

Regulatory

ul

Properties

Modulus

22.000MPa

Strength

275MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
22000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
275 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
21200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
435 MPa
370 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
90 kJ/m²
90 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
18 kJ/m²
17 kJ/m²
18 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
330 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
240 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,55 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,72 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1017 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more