Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

B3 GK 30 natural (2719)

PA6 GB30

AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROMIDĀ®

B3 GF 40 1 L black (4581)

PA6 + PP GF40

AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

11.000MPa

Strength

150MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

B3 ICF 30 black (5119)

PA6 CF30

AKROMIDĀ® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

200MPa

Impact

55kJ/mĀ²

AKROMIDĀ® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMIDĀ®

A3 ICF 20 black (5102)

PA66 CF20

AKROMIDĀ® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

16.000MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

PRECITEĀ®

P3 GF 50 natural (6944)

PBT GF 50

PRECITEĀ® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

185MPa

Impact

60kJ/mĀ²

PRECITEĀ® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMIDĀ®

Preliminary

A28 GF 35 6 black (7278)

PA66 GF35

AKROMIDĀ® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

85kJ/mĀ²

AKROMIDĀ® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry

AKROMIDĀ®

UL

A3 GF 30 FR black (7751)

PA66 GF30 FR(40)

AKROMIDĀ® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.

Modulus

10.500MPa

Strength

150MPa

Impact

67kJ/mĀ²

AKROMIDĀ® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.

135363780

AKROMIDĀ®

A3 GF 50 8 natural (7291)PA66 GF50

AKROMIDĀ® A3 GF 50 8 natural (7291) is 50% glass fiber reinforced PA6.6 with very high rigidity and strength. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances.

Regulatory

eu102011fda

Properties

Modulus

17.400MPa

Strength

265MPa

Impact

115kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17400 MPa
13400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
265 MPa
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,9 %
3,9 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
115 kJ/mĀ²
120 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
24 kJ/mĀ²
29 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

General properties

Density

ISO 1183

23Ā°C
1,57 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Water absorption

ISO 62

23Ā°C, saturated
3,7 - 4,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more