AKROMIDĀ®
B3 GK 30 natural (2719)
PA6 GB30
AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.400MPa
70MPa
30kJ/mĀ²
AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
AKROMIDĀ®
B3 GF 40 1 L black (4581)
PA6 + PP GF40
AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
11.000MPa
150MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
AKROMIDĀ®
B3 ICF 30 black (5119)
PA6 CF30
AKROMIDĀ® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
23.000MPa
200MPa
55kJ/mĀ²
AKROMIDĀ® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROMIDĀ®
A3 ICF 20 black (5102)
PA66 CF20
AKROMIDĀ® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
16.000MPa
190MPa
50kJ/mĀ²
AKROMIDĀ® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
PRECITEĀ®
P3 GF 50 natural (6944)
PBT GF 50
PRECITEĀ® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.
17.000MPa
185MPa
60kJ/mĀ²
PRECITEĀ® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.
AKROMIDĀ®
A28 GF 35 6 black (7278)
PA66 GF35
AKROMIDĀ® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
11.500MPa
210MPa
85kJ/mĀ²
AKROMIDĀ® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
AKROMIDĀ®
A3 GF 30 FR black (7751)
PA66 GF30 FR(40)
AKROMIDĀ® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.
10.500MPa
150MPa
67kJ/mĀ²
AKROMIDĀ® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.
AKROMIDĀ®
T5 GF 40 8 black (6458)PPA GF40
AKROMIDĀ® T5 GF 40 8 black (6458) is a 40% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to ACS, WRAS and NSF 61. It is suitable for applications that are in contact with cold and hot drinking water. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.
Regulatory
Properties
15.000MPa
245MPa
80kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.