AKROMID®
B3 ICF 10 black (5118)
PA6 CF10
AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
8.000MPa
120MPa
50kJ/m²
AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROLOY®
PA LGF 50 natural (5504)
PA66+PA6I/6T LGF50
AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance
19.000MPa
290MPa
100kJ/m²
AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance
AKROMID®
C3 GFM 15/25 1 black (6653)
PA66+PA6 (GF15+M25)
AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability
8.000MPa
120MPa
50kJ/m²
AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability
PRECITE®
P3 ICF 20 black (6947)
PBT CF20
PRECITE® P3 ICF 20 black (6947) is a 20% carbon fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as low Density and good tribological properties
16.000MPa
150MPa
50kJ/m²
PRECITE® P3 ICF 20 black (6947) is a 20% carbon fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as low Density and good tribological properties
AKROMID®
B3 GF 30 ECO black (7923)
PA6 GF30
AKROMID® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.
9.500MPa
155MPa
75kJ/m²
AKROMID® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.
AKROMID®
B3 GF 30 9 RM-M black (3099)
PA6+X GF30
AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
10.500MPa
170MPa
70kJ/m²
AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
AKROMID®
B3 CGM 6/20 black (4362)
PA6 (CF6+GF20)
AKROMID® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity
11.000MPa
175MPa
60kJ/m²
AKROMID® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity
AKROLOY®
PARA GF 50 HU black (8596)PARA GF50
AKROLOY® PARA GF 50 HU black (8596) is a 50% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state.Even in conditioned state, it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.
Features
Regulatory
Properties
19.700MPa
295MPa
78kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Glass transition temperature
ISO 11357-2
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.