AKROMID®
B3 GF 30 black (2493)
PA6 GF30
AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
75kJ/m²
AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GK 30 natural (2719)
PA6 GB30
AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.400MPa
70MPa
30kJ/m²
AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
B3 GF 30 RM-M natural (3291)
PA6 + X GF30
AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
11.000MPa
165MPa
70kJ/m²
AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
AKROMID®
B3 GK 50 natural (3690)
PA6 GB50
AKROMID® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage
5.700MPa
75MPa
42kJ/m²
AKROMID® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage
AKROMID®
B3 GF 40 1 L black (4581)
PA6 + PP GF40
AKROMID® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
11.000MPa
150MPa
70kJ/m²
AKROMID® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
AKROMID®
B3 GF 60 1 black (4644)
PA6 GF60
AKROMID® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
21.000MPa
250MPa
90kJ/m²
AKROMID® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
AKROLOY®
PA ICF 20 black (5268)
PA66 + PA6I/6T CF20
AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
17.000MPa
200MPa
45kJ/m²
AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMID®
A3 GF 35 1 HU natural (8418)PA66 GF35
AKROMID® A3 GF 35 1 HU natural (8418) is a 35% glass fibre reinforced, heat ageing resistant polyamide 6.6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry.
Features
Regulatory
Properties
11.900MPa
216MPa
Na
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.