AKROMID®

B3 GF 15 1 natural (2461)

PA6 GF15

AKROMID® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color

AKROMID®

A3 1 S3 15 natural (2892)

PA66-I

AKROMID® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E

AKROMID®

B3 GK 30 natural (2719)

PA6 GB30

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROLEN®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

AKROMID®

A3 GF 30 1 S3 black (3502)

PA66-I GF30

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

Modulus

8.000MPa

Strength

170MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

AKROMID®

B3 GF 50 8 natural (4301)

PA6 GF50

AKROMID® B3 GF 50 8 natural (4301)- PA6, 50% glass fiber, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 8 natural (4301)- PA6, 50% glass fiber, FDA, EU 10/2010, food contact, kitchen and household appliances

AKROTEK®

PK-HM natural (4773)

PK

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

133343580

PRECITE®

Preliminary

P3 ICF 30 black (6948)PBT CF 30

PRECITE® P3 ICF 30 black (6948) is a medium viscous polybutylene terephthalate (PBT) with 30% recycled carbon fiber. Despite lower density compared to PBT with glass fiber reinforcement, the product has very high strength and toughness as well as high dimensional stability. The good tribological properties and improved surface finish make it the material of choice for precision components in the automotive, mechanical engineering, E&E and household goods industries.

Features

surface modified
recycled content
reduced density
tribological modified
E&E
Sports & leisure
lightweight construction

Properties

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
23500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
32500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
300 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,41 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Water absorption

ISO 62

23°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
103 Ω

Rheological Properties

MVR

ISO 1133

250°C/2,16kg
10 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more