AKROMIDĀ®

B3 GK 50 natural (3690)

PA6 GB50

AKROMIDĀ® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/mĀ²

AKROMIDĀ® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

AKROMIDĀ®

B3 GF 60 1 black (4644)

PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMIDĀ®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROLOYĀ®

Preliminary

PA GF 30 natural (6412)

PA66+PA6I/6T GF30

AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

10.200MPa

Strength

200MPa

Impact

70kJ/mĀ²

AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMIDĀ®

A3 GF 30 3 black (21005)

PA66 GF30

AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

170MPa

Impact

55kJ/mĀ²

AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry

AKROMIDĀ®

B3 GF 30 2 S1 grey (4289)

PA6-I GF30

AKROMIDĀ® B3 GF 30 2 S1 grey (4289) - PA 6, 30% glass fiber reinforced, impact modified and UV stabilised, for industrial applications, housings and covers, automotive

Modulus

8.500MPa

Strength

120MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 2 S1 grey (4289) - PA 6, 30% glass fiber reinforced, impact modified and UV stabilised, for industrial applications, housings and covers, automotive

AKROMIDĀ®

B3 GF 15 1 black (2482)

PA6 GF15

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

132333480

AKROMIDĀ®

A28 LGF 50 9 black (7705)PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) is an easy flowing PA6.6 with 50% long glass fibre reinforcement which leads to an extraordinary high stiffness and strength even at high temperature. The material distinguishes itself due to its isotropic mechanical properties as well as increased creep resistance and higher heat deflection temperature. The excellent fatigue performance, high energy absorption in the event of a crash and low shrinkage make it the product of your choice for technical parts e.g. oil pan.

Features

easy flow
process improved

Properties

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18000 MPa
14200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
2,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
95 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
45 kJ/mĀ²
45 kJ/mĀ²

Izod impact strength

ISO 180/1A

23Ā°C | d.a.m.
90 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
60 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,25 10ā»ā“/K
0,75 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,57 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more