AKROMID®

A3 GF 30 6 black (6736)

PA66 GF30

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMID®

A3 GF 30 3 black (21005)

PA66 GF30

AKROMID® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

170MPa

Impact

55kJ/m²

AKROMID® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry

AKROMID®

B28 GM 10/20 1 LT black (7749)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

Modulus

6.300MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

AKROMID®

UL

B3 GF 30 FR orange (7857)

PA6 GF 30 FR(40)

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

Modulus

10.500MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

AKROLEN®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

AKROMID®

B28 GF 30 6 LT black (6931)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

AKROMID®

Preliminary

B3 GF 30 ECO black (7923)

PA6 GF30

AKROMID® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

132333480

AKROMID®

A3 GF 20 1 natural (1261)PA66 GF20

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

Features

heat stabilised 130

Properties

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7200 MPa
4600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
7000 MPa
5000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
235 MPa
165 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
60 kJ/m²
86 kJ/m²
48 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
9 kJ/m²
8 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
210 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 °C
130 -150 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,28 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,3 - 2,5 %

Water absorption

ISO 62

23°C, saturated
6,7 - 7,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
1,3 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.