HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GK 50 black (2311)

PA6 GB50

AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

AKROMID®

A3 GF 60 1 natural (2396)

PA66 GF60

AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.

Modulus

20.500MPa

Strength

260MPa

Impact

102kJ/m²

AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.

AKROMID®

A3 GM 20/10 S1 black (4817)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

AKROMID®

B3 ICF 30 black (5119)

PA6 CF30

AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

200MPa

Impact

55kJ/m²

AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

A3 GF 50 6 black (6860)

PA66 GF50

AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

18.000MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

Preliminary

A28 GF 35 6 black (7278)

PA66 GF35

AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

85kJ/m²

AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry

AKROMID®

B28 GM 10/20 1 LT black (7749)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

Modulus

6.300MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

131323380

AKROMID®

Preliminary

B3 GF 40 S1 black (8647)PA6-I GF40

EXPERIMENTAL GRADE AKROMID® B3 GF 40 S1 black (8647) is a 40% glass fiber reinforced, impact modified polyamide 6. It is characterised by a high cold impact a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Features

impact modified
reduced density

Properties

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
105 kJ/m²
125 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
26 kJ/m²
38 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,42 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0.25 - 0.45 %
0.7 - 0.9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
100 mm
310 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more