Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
B3 GK 50 black (2311)
PA6 GB50
AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
5.700MPa
75MPa
42kJ/m²
AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
AKROMID®
A3 GF 60 1 natural (2396)
PA66 GF60
AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
20.500MPa
260MPa
102kJ/m²
AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
AKROMID®
A3 GM 20/10 S1 black (4817)
PA66-I (GF20+GB10)
AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage
6.900MPa
130MPa
80kJ/m²
AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage
AKROMID®
B3 ICF 30 black (5119)
PA6 CF30
AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
23.000MPa
200MPa
55kJ/m²
AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROMID®
A3 GF 50 6 black (6860)
PA66 GF50
AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
18.000MPa
250MPa
105kJ/m²
AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A28 GF 35 6 black (7278)
PA66 GF35
AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
11.500MPa
210MPa
85kJ/m²
AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
AKROMID®
B28 GM 10/20 1 LT black (7749)
PA6 (GF10+GB20)
AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage
6.300MPa
110MPa
40kJ/m²
AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage
AKROMID®
B28 GF 30 S3 natural (8348)PA6-I GF30
AKROMID® B28 GF 30 S3 natural (8348) is a 30% glass fibre reinforced, easy flowing polyamide 6. Furthermore, the material is impact modified and therefore characterised by a higher dry impact strength compared to standard PA 6 GF 30. Its high strength and stiffness make it the material of your choice for technical applications in industrial engineering and in the furniture industry. The material has a light inherent color.
Features
Properties
8.900MPa
160MPa
100kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.