Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
B3 GK 50 black (2311)
PA6 GB50
AKROMIDĀ® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
5.700MPa
75MPa
42kJ/mĀ²
AKROMIDĀ® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
AKROMIDĀ®
A3 GF 60 1 natural (2396)
PA66 GF60
AKROMIDĀ® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
20.500MPa
260MPa
102kJ/mĀ²
AKROMIDĀ® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
AKROMIDĀ®
B3 GF 15 1 natural (2461)
PA6 GF15
AKROMIDĀ® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color
6.100MPa
120MPa
52kJ/mĀ²
AKROMIDĀ® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color
AKROMIDĀ®
B3 GK 30 natural (2719)
PA6 GB30
AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.400MPa
70MPa
30kJ/mĀ²
AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage
AKROMIDĀ®
B3 GF 30 9 RM-M black (3099)
PA6+X GF30
AKROMIDĀ® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
10.500MPa
170MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
AKROMIDĀ®
B3 CGM 6/20 black (4362)
PA6 (CF6+GF20)
AKROMIDĀ® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity
11.000MPa
175MPa
60kJ/mĀ²
AKROMIDĀ® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity
AKROMIDĀ®
B28 GF 60 9 black (4662)
PA6 GF60
AKROMIDĀ® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
21.000MPa
250MPa
90kJ/mĀ²
AKROMIDĀ® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
AKROMIDĀ®
B3 GF 30 1 L black (4365)PA6+PP GF30
AKROMIDĀ® B3 GF 30 1 L black (4365) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 30 1 L black (4365) is particularly superior to calcium chloride (CaClā).
Features
Properties
8.800MPa
140MPa
60kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.