PRECITE®

Preliminary

P3 GF 15 4 natural (8429)

PBT-I GF15

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

Modulus

5.000MPa

Strength

85MPa

Impact

55kJ/m²

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

AKROTEK®

Preliminary

PK-VM GF 50 natural (8683)

PK GF50

AKROTEK® PK-VM GF 50 natural (8683) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

190MPa

Impact

80kJ/m²

AKROTEK® PK-VM GF 50 natural (8683) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

Preliminary

B28 GM 10/20 6 black (8640)

PA6 (GF10+GB20)

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

Modulus

5.500MPa

Strength

100MPa

Impact

50kJ/m²

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

AKROMID®

A3 S1 black (1071)

PA66-I

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 black 950089 (1071) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

AKROLEN®

PP GFM 25/15 black (1415)

PP (GF25+M15)

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 black (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability.

AKROMID®

B3 GK 50 black (2311)

PA6 GB50

AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

129303179

AKROMID®

Preliminary

B3 GF 40 1 black (8353)PA6 GF40

AKROMID® B3 GF 40 1 black (8353) is a 40% glass fiber reinforced polyamide 6 which is characterised by excellent bonding to LSR (liquid silicone rubber). Furthermore, the material shows high stiffness and strength. On top of that, it is heat stabilised and low in emissions and therefore perfectly suitable for technical applications in industrial engineering and in the automotive industry, such as airbag applications.

Features

heat stabilised 130
adhesion modified

Properties

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
13000 MPa
8300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
195 MPa
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
12259 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
305 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
115 kJ/m²
85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
16 kJ/m²
23 kJ/m²
12 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more