AKROMID®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROLOY®

Preliminary

PARA FGF 50 1 black (8186)

PARA FGF50

AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing

Modulus

19.000MPa

Strength

295MPa

Impact

75kJ/m²

AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing

PRECITE®

Preliminary

P3 GF 20 8 natural (8456)

PBT GF20

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

7.200MPa

Strength

125MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

PRECITE®

Preliminary

P3 GF 15 4 natural (8429)

PBT-I GF15

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

Modulus

5.000MPa

Strength

85MPa

Impact

55kJ/m²

PRECITE®P3 GF 15 4 natur (8429) - PBT, 15% GF, hydrolysis stabilised, good stiffness, good toughness, GMA free, low moisture absorption, dimensional stability, fulfills VW-50136 standard.

AKROMID®

B28 GF 30 S3 white (8349)

PA6-I GF30

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

150MPa

Impact

94kJ/m²

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

PRECITE®

Preliminary

E GF 45 ECO black (8284)

PET GF45

PRECITE® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

Modulus

16.100MPa

Strength

200MPa

Impact

65kJ/m²

PRECITE® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CR black (8313)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

129303180

AKROMID®

B3 GF 40 black (6077)PA6 GF40

AKROMID® B3 GF 40 black (6077) is a 40% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Properties

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
13000 MPa
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
205 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
12600 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
40°C | d.a.m.
-
110 kJ/m²
106 kJ/m²
105 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
40°C | d.a.m.
-
20 kJ/m²
30 kJ/m²
15 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23°C, saturated
5,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more