AKROMID®
B3 ICF 30 AM black (7451)
PA6 CF30
AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
20.000MPa
190MPa
45kJ/m²
AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
PRECITE®
P3 black (7811)
PBT
PRECITE® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.
2.600MPa
60MPa
90kJ/m²
PRECITE® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.
AKROMID®
C28 GF 25 FRT grey (7560)
PA-Blend
AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.
11.000MPa
135MPa
60kJ/m²
AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.
AKROMID®
C28 GF 25 FRT blue (7986)
PA-Blend
AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.
11.000MPa
145MPa
60kJ/m²
AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.
PRECITE®
P3 GF 30 9 FR black (8424)
PBT GF30 FR(40)
PRECITE® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
10.500MPa
122MPa
50kJ/m²
PRECITE® P3 GF 30 9 FR black (8424) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
AKROMID®
B3 GF 40 1 HU black (8415)
PA6 GF40
AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.
AKROMID®
NEXT B3 GF 30 1 L CR black (8313)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
A3 GF 30 1 L black (4436)PA66+PP GF30
AKROMID® A3 GF 30 1 L black (4436) is a PA6.6-PP-blend with reduced density compared to standard PA66. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® A3 GF 30 1 L black (4436) is particularly superior to zinc chloride (ZnCl₂).
Features
Properties
8.400MPa
150MPa
77kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.