AKROMID®

C28 GF 25 FRT grey (8133)

PA-Blend

AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

150MPa

Impact

NA

AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.

AKROMID®

Preliminary

NEXT 5.10 3 GF 30 black (8467)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

PRECITE®

Preliminary

P3 GF 20 8 natural (8456)

PBT GF20

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

7.200MPa

Strength

125MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

PRECITE®

Preliminary

K GF 50 8 black (8446)

PBT+PET GF50

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

17.500MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

AKROMID®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

PRECITE®

Preliminary

E GF 30 black (7814)

PET GF30

PRECITE® E GF 30 black (7814) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

11.000MPa

Strength

170MPa

Impact

50kJ/m²

PRECITE® E GF 30 black (7814) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

128293080

AKROMID®

B3 1 natural (2499)PA6

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

Features

heat stabilised 130

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Water absorption

ISO 62

23°C, saturated
9,0 - 10,0 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more